| 40-001 |
- Anti-drip additive or synergist
- Flame retardant
- Thinner clear polycarbonate applications
- 100% non-halogenated silicone polymer
- Active at low use level
|
- Reaches UL 94 V-0 rating at 1 mm with synergists
- Reaches UL 94 V-0 at 1.5 mm
- Haze at 2%
- No impact on Young’s modulus and tensile maximum force at traction.
|
| KPBS |
- Chemical Name : Potassium Perfluorobutane Sulfonate
- Molecular formula : C4F9O3KS
- Molecular Weight: 338.12
- CAS No. : 29420-49-3
- Appearance: White Powder
- Melting Point (℃) : Around 265℃
- Solubility in Water wt% at 25°C : 5%
|
- effective flame retardant in polycarbonate at use levels as low
- For most effective incorporation, the additive be initially dispersed into a 10% or more masterbatch and then compounded into the final plastic blend
- Dispersion can be achieved effectively with typical PC processing equipment without the use of synergists.
- V0 in clear polycarbonate at 1/8" (3 mm) thickness and 0.6 wt%
- V0 in PC and PC/ABS
|
| KSS |
- Eco-friendly material, Fluorine, Bromine, Chlorine, Phosphorus Free
- Performance with small amount addition(0.4-1%)
- About 10% slight decrease in PC property
- No significant influence on transparency
- Excellent thermal stability, only about 5% decomposition at 450 ℃
|
- UL94 V0 (3.2mm) in pure or tinted PC
- Mainly used in granule manufacturing process or injection molding
- Best flame retardant for PC that must be used at high temperatures
- Due to the unique resin structure no precipitation occurs in any application
|
| HES |
- Excellent water resistance
- Little effect on resin properties
- Little effect on the heat deflection temperature of the resin
|
- Suitable for translucent or opaque flame retardant PCs
- UL94 V0 achieved with low addition
|
| HES2-FR |
- non-halogen mixed metal salt of aromatic sulfonates
|
- The most effective flame retardant for transparent and and opaque PC
|
APP(Ammonium
Polyphosphate) |
- CAS No.: 68333-79-9
- P %（w/w）: 31.0-32.0
- N %（w/w）: 14.0-15.0
- pH Value(10% suspension liquid): 5.5-7.0
- Moisture%（w/w）: ≤0.25
- Thermal Decomposition Temperature, ℃: ≥275
- Density(25℃ kg/L) : About 1.9
- Bulk Density (25℃ kg/L) : About 0.7
- Viscosity（25℃，10% suspension ）mpa.s : ≤100
- Solubility （g/100cm3 water ）: About 0.5
- Average Particle size (um) : About 15
|
- Polyurethane foam, UP resins, epoxy resins
- flame retardant in various manufactured goods made from fiber, timber, rubbeer and plastics
- the polymer chemicals allow PP to achieve UL94-V0 flammability rating When used for producing electronic components
|
Melamine
Cyanurate (MCA) |
- CAS NO.: 37640-57-6
- MCA(%)≥: 99.5
- Residual Cyanuric Acid(%) : ≤0.2
- Residual Melamine(%) : ≤0.001
- Whiteness : ≥96
- Dry Weight Loss(%) : ≤0.2
- pH Value : 5-7
- Specific gravity(g/cm3) : 1.7
- Bulk Density (g/cm3) : 0.3-0.4
- Water Solubility(g/100ml water) : 0.002(20℃)
|
- Halogen-free flame retardant for PA6, PA66
- Achieve UL94-V0
- It can offer superior electrical and mechanical properties.
- As a halogen-free flameproof material, it possesses low smoke density, toxicity and low corrosion
|
Melamine
Polyphosphate(MPP) |
- CAS NO.: 218768-84-4
- P % : 15.0±1.0
- Moisture% : ≤0.2
- Thermal Decomposition Temperature ℃ : ≥330
- Particle size ㎛ : ≤5
- Specific gravity g/cm3 : About 1.6
- Bulk Densityg/cm3 : About 1.5"
|
- It is mostly applicable to PBT and PA, especially PA6, PA66, glass fiber reinforced PA6, PA66
- It conforms to European Environmental protection with low toxicity and no halogen.
- It does not require any special screws combination or special glass fiber.
- Different from general halogenated flame retardants, it can protect both equipment and mould from corrosion.
- It is extremely suitable for glass fiber reinforced nylon dut to the outstanding thermal stability
|
2-Carboxyethyl(phenyl)
phosphinicacid (CEPPA) |
- CAS No. : 14657-64-8
- Appearance : White powder or crystal
- Purity(HPLC): ≥99.0%
- Melting ponint : 156-161℃
- P %: ≥14.0±0.5%
- Acid Value : 522±4mgKOH/g
- Fe %: ≤0.005%
- Chloride Content : ≤0.01%
- Moisture : ≤0.5%"
|
- This product is soluble in water, glycol and other solvents.
- Flame retardant which can be used in all PET and PET-based formulations and does not decompose or smell due to excellent thermal stability
- Act as antistatic agent in PET formulation
- The amount of PTA and EG polymerization is about 2.5 ~ 4.5%, when added to PET sheet about 0.35-0.60%, the LOI of the final flame retardant product is about 30 ~ 36%
|
| DOPO(HCA) |
- Chemical Name: 9,10-Dihydro-9-oxa-10-phosphaphenanthrene 10-oxide
- CAS No.: 35948-25-5
- Purity(HPLC): ≥99.5%
- OPP Content(HPLC): ≤0.1%
- Cl (mg/kg): ≤20
- P (%): ≥14.0
- Zn (mg/kg): ≤5
- Na (mg/kg): ≤30
- Melting point: 117-120℃"
|
- It is white crystals or powder and easily soluble in methanol, ethanol, chloroform, benzene and Toluene but it is insoluble in water.
- It is applied in epoxy resins PET and PA and it can be used in plastics for electronics or PCB
- DOPO is additive flame retardant, which is characterized by high thermal stability, strong oxidation resistance and great water resistance.
- Its flame-retardant performance is better than that of the general phosphate esters.
|
Bisphenol A bis-
(diphenylphosphate)-
Biphosphate(BDP) |
- CAS No.: 5945-33-5
- Appearance : Colorless liquid
- Specific gravity: 1.258
- Viscosity (40℃, cps): 1,400 ~ 2,200
- Moisture: 0.1% max
- Acid Value (KOH mg/g): 0.1 max
- Phenol Content: 0.1% max
- TPP Content: 3% max
- P Content: About 9%
|
- It is used for diversified engineering plastics such as PPO(Polyphenylene oxide), Polycarbonateblends, PC/ABS and PPO/HIPS.
|
| TPP |
- Synonym: Phosflex TPP; Reofos TPP; Disflamoll TP
- CAS No.: 115-86-6
- Appearance: White, flaked solids
- Color APHA (Pt-Co) : 50 max
- Phenol Content : 0.05%↓
- Acid Value (mgKOH/g) : 0.03 max
- Moisture(W/W%) : 0.1
|
- TPP is commonly used as a fire retardant in sundry plastics and resins such as phenolic resin, cellulose resin, epoxy resin, PVC, PP, PC, ABS and PC/ABS.
- It can function as a non-flammable plasticizer or additive in cellulose for photographic film, polyester and polyurethane.
|
| RDP |
- Chemical Name: Tetraphenyl resorcinol bis(diphenyl phosphate)
- CAS No.: 57583-54-7
- Appearance: Colorless or yellowish, transparent, viscous liquid
- Color (APHA) : ≤80
- Acid Value (mg KOH/g) : ≤0.1
- Moisture (wt. %) : ≤0.05
- P (wt. %): 10.8
- TPP Content (wt. %) : ≤5.0
- Phenol Content (ppm) : ≤500
- Specific gravity (25°C, g/cm3): 1.315±0.010
- Viscosity (25°C, mPaㆍs): 500-800
|
- RDP is a halogen-free and phosphate-based flame retardant, which offers advantages like low volatility and superior thermal stability. it can meet the need engineered resins for high temperature
- It is often used for PC/ABS, PPO/HIPS
|
| CDP |
- Chemical Name: Cresyl diphenyl phosphate
- CAS No.: 26444-49-5
- Color (APHA): ≤100
- Acid Value (mgKOH/g): ≤0.1
- Moisture (wt. %): ≤0.1
- Refractive index: 1.560±0.005
- Specific gravity (25°C, g/cm3): 1.210±0.010
- PContent (wt. %): 9.1
- Free phenol Content (PPM): ≤200
- Viscosity (25°C, mPaㆍs): 34-38
|
- Excellent resin compatibility, oil resistance, excellent electrical properties, hydrolysis stability, low volatility and low temperature flexibility/li>
- Mainly used for soft PVC, PVB Chloro Polyethylene, natural rubber NBR, soft PU foam
|
| TCPP |
- Chemical Name: Tris(1-chloro-2-propyl) phosphate
- CAS No.: 13674-84-5
- Acid Value (mg KOH/g): ≤0.07
- Moisture (wt. %): ≤0.07
- Specific gravity (25°C, g/cm3): 1.293±0.005
- P % (wt. %): 9.5
- Cl % (wt. %): 32.5
- Viscosity (25°C, mPaㆍs): 65-72
|
- It is basically a flame retardant used for hard / soft PU foam, and has excellent thermal stability, hydrolysis stability, low viscosity, and excellent resin compatibility.
- It can be used as flame retardant of adhesive or PVC besides PU
|
| TDCP |
- Appearance : Tris(1,3-dichloroisopropyl) phosphate
- CAS No.: 13674-87-8
- Color (APHA): ≤60
- Acid Value (mg KOH/g): ≤0.07
- Moisture (wt. %): ≤0.07
- PContent (wt. %): 7.1
- ClContent (wt. %): 49.0
- Specific gravity (25°C, g/cm3): 1.512±0.005
- Viscosity (25°C, mPaㆍs): 1500-1800
|
- Basic Chlorine Phosphate Flame Retardant for PU Foam with Excellent Stability and Low Cost
- Suitable for polyurethane, epoxy, phenolic resin
- When used in polyurethane foam, meets standards such as California TB 117, FMVSS 302, UL 94 HF-1, BS 5852 Crib 5, DIN 75200 and CSE RF4 Class 1
|